The influence of prior austenite deformed at different temperature on the subsequent continuous cooling bainitic transformation has been investigated in an C-Ma-Cr-Ni-Mo plastic die steel. The results show that the prior deformation in low temperature region of austenite retards significantly the bainitic transformation. For the same continuous cooling schedule, as austenite deformed at lower temperature, the quantity of the classical sheaf-like bainite becomes less. The present results show that severe deformation leads to mechanical stabilization of austenite and causes the difficulty of bainitic ferrite propagation into the austenite.
关键词:
plastic die steel
,
null
,
null
,
null
,
null
刘东升
,
王国栋
,
刘相华
,
甄立冬
,
苏永科
,
徐辉
金属学报
采用膨胀法结合金相分析建立了P20钢的CCT曲线,根据动态CCT曲线，提出P20钢轧后控冷预硬化工艺．与常规热处理条件相比，形变热处理条件下的奥氏体具有较高的稳定性.变形后以0．2—0．02℃／s连续冷却时，主要发生贝氏体相交，而多边形铁素体相变被抑制．变形可使奥氏体机械稳定化，阿氏体相变推迟至较低温度下完成.P20钢轧后在贝氏体相变区缓冷获得粒状贝氏体组织，实现在线预硬化，硬度达到35—38．
关键词:
P20塑料模具钢
,
hardening
,
transformation
,
granular bainite
,
deformed austenite
段丽丽
,
张铮
,
李晓成
,
吴晓春
材料热处理学报
对新开发大截面贝氏体塑料模具钢SDP2在极低冷速下的过冷奥氏体连续冷却转变过程和相变动力学进行了研究.采用DIL805A高精度差分热膨胀仪测量SDP2钢线膨胀行为,利用SEM分析冷却转变产物;根据JMA公式计算SDP2钢贝氏体相变激活能和Avrami指数.结果表明,SDP2钢过冷奥氏体连续冷却过程包含珠光体、贝氏体和马氏体转变,而无铁素体转变;当冷速大于0.02C/s时,转变产物以下贝氏体或马氏体为主;小于0.02℃/s时,以上贝氏体或粒状贝氏体为主,并出现珠光体.SDP2钢贝氏体转变的激活能为117 k J/mol,SDP2钢在不同冷速下贝氏体转变动力学指数Avrami指数n≈2 ～3,经分析计算所得的Avrami指数值所对应的显微组织形态和实验所观察到的显微组织相符合.
关键词:
塑料模具钢
,
CCT
,
贝氏体相变
,
热膨胀
,
动力学
刘国勇
,
王宽宽
,
董栗明
,
宫世创
,
朱冬梅
,
张少军
材料热处理学报
通过间接热力耦合对120 mm厚718塑料模具钢连续淬火、多道次淬火及变频幅淬火3种在线淬火工艺冷却过程温度场和应力/应变场进行了三维数值模拟.结果表明:与连续淬火工艺相比,多道次淬火工艺可获得较小的表心温差、等效塑性应变及等效应力最大值,但等效应力平均值有所增大,且淬火时间较长;与前两种工艺相比,变频幅淬火工艺可获得最小的表心温差、等效塑性应变、等效应力,以及比多道次淬火工艺较短的淬火时间,且由于关闭了部分喷嘴,起到了节水节能的作用,为优化大尺寸718塑料模具钢在线淬火工艺提供参考.
关键词:
塑料模具钢
,
在线淬火
,
变频幅
,
数值模拟