张延忠
,
年素珍
金属学报
本文报道三种新型铁基微晶合金Fe_(73)Cu_(1.2)Nb_(3.2)Si_(12.5)B_(10)(合金1),Fe_(73.1)Cu_1Nb_(1.5)Si_(1.25)B_(10)(合金2)及Fe_(73)Cu_1Zr_3C_(0.5)Si_(12.5)B_(10)(合金3),它们具有μ'_i≥5×10~4的高相对起始磁导率、Hc≤1.0A/m的低矫顽力、在相当宽频率范围内的高有效磁导率、低铁芯损耗和窄脉冲条件下的高脉冲磁导率。在f=1kHz和H_m=0.4A/m条件下,相对有效磁导率μ’_5的最佳值为16×10~4,超过了Yoshizawa报道的μ’_5=10×10~4。最佳铁损值为P_(5/50k)=57.9W/kg、P_(2/100k)=30.2W/kg和P_(3/100k)=68W/kg,也超过了Yoshizawa报道的P_(2/100k)=38.9W/kg。这些合金都具有优良的磁性稳定性;在130℃下保温216h后起始磁导率不变,合金的主晶相是Fe_(75+y)Si_(25-y)型有序固溶体,晶粒的平均直径为10～20nm。
关键词:
微晶合金
,
relative initial permeability
,
effective permeability
,
coercivity
,
core lose
ZHANG Yanzhong
,
NIAN Suzhen Shanghai Iron and Steel Research Institute
金属学报(英文版)
Three new Fe-based microcrystalline alloys,i.e.,Fe_(73.1)Cu_(1.2)Nb_(3.2)Si_(12 5)B_(10), Fe_(73)Cu_1Nb_(1.5)Mo_2Si_(12.5)B_(10) and Fe_(73)Cu_1Zr_3C_(0.5)Mo_Si_(12.5)B_(10),were developed with su- perior magnetic properties.e.g.,high relative initial permeability of μ_i~15×10~4,low coercivity of H_c1.0A/m,high effective permeability and low core losses in a consid- crable wide frequency range and high pulse-magnetic permeability under narrow pulse. The optimum value of relative effective permeability,μ_5~1 is 16×10~4 under condition of f=1 kHz and H_m=0.4 A/m.The optimum values of core loss reach 57.9 30.2 and 68 W/kg under condition of f=50.100.100 KHz and B_m=0.5,0.2,0.3 T,respectively. These three alloys have superior stability of magnetic properties.Initial permeability may be not changed during heating at 130℃ up to 216 h.The main crystalline phase is ordered phase Fe_((75)+y)Si_((25)-y) which is ultrafine particles of average size 10—20 nm.
关键词:
microcrystalline alloy
,
null
,
null
,
null
,
null
,
null