范鹏
,
周渝生
,
杨天钧
,
董一诚
,
魏寿昆
金属学报
在1300—1500℃的温度范围内测得碳饱和铁液中Nb的溶解度与温度的关系为:lg[％Nb]_(max)=-5899/T+3.28.为避免碳化银沉淀对测定的干扰,采用了一种扩散平衡法进行测定,还做了碳化铌过饱和析出实验,证实了扩散平衡法测定结果的可靠性。
关键词:
Nb
,
Fe-C-Nb alloy
,
solubility
,
thermodynamics
冯水富
,
周继程
金属学报
用改进的半导体材料生长中的液相外延设备测定了GaAs在Bi中溶解度。根据测定结果,获得了富Bi侧的Bi-GaAs二元平衡图。同时发现,在所研究的温度范围内相同的溶解时间内的溶解量与饱和溶解量之比与温度的关系也各不相同。这一现象似可认为是某些金属间溶解过程中的普遍特性。
关键词:
液相外延
,
solubility
,
phase diagram
FENG Shuifu ZHO U Jicheng Shanghai Institute of Metallurgy
,
Academia Sinica
,
Shanghai
,
China ZHOU Jicheng
,
Shanghai Institute of Metallurgy
,
Academia Sinica
,
Shanghai 200050
,
China
金属学报(英文版)
A modified liquid phase epitaxy apparatus for semiconductor materials was used to measure the solubility of GaAs in Bi.Two phase diagrams rich in Bi under H_2 and N_2 atmospheres were obtained according to the results of measurement.A new phenomenon,in which the parameter Q value(quantity of GaAs di...
关键词:
solubility
,
null
,
null
LI Laifeng XING Zhongshu Institute of Metal Research
,
Academia Sinica
,
Shenyang
,
China XING Zhongshu
,
professor
,
Institute of Metal Research
,
Academia Sinica
,
Shenyang 110015
,
China
金属学报(英文版)
The solubilities of Ce,Nd and Y in α-Fe at 873 to 1153 K have been deter mined by means of electron microprobe quantitative analyses.The temperature dependences of the solubilities were obtained from the experimental data.The results have been compared with those deter- mined by three other technigu...
关键词:
α-Fe
,
null
,
null
,
null
,
null
谢晨辉
,
周华堂
,
彭宇
硬质合金
doi:10.3969/j.issn.1003-7292.2013.10.002
本文以工业纯钴粉、钴基合金、硬质合金作为研究对象,分别运用X射线衍射、金相、扫面电镜能谱、EBSD等分析技术,并结合晶体学的相关知识研究了钴的基本特性、微观结构及其切变机制.通过研磨工业纯钴粉,比较分析研磨前后X射线衍射分析结果,定性描述了钴粉的α-Co向ε-Co的转变过程;实验制备了不同固溶W含量...
关键词:
粘结相
,
固溶度
,
ε-马氏体
,
切变机制
,
EBSD
,
位错
,
层错
,
孪晶
ZHAI Qijie
,
HU Hanqi
,
University of Science and Technology Beijing
,
Beijing
,
China HU Hanqi
,
Professor
,
Faculty of Foundry
,
University of Science and Technology Beijing
,
Beijing 100083
,
China
金属学报(英文版)
The expressions of the dependence of nitrogen solubility in molten gray cast iron on the temperature and composition of the melt were proposed under the condition of foundry practice. Three gray cast iron specimens with different compositions were examined in good agreement with the derived expressi...
关键词:
gray cast iron
,
null
,
null
滕雅娣
,
孙晓龙
,
黄鑫龙
,
盛永刚
,
周华锋
功能材料
doi:10.3969/j.issn.1001-9731.2015.09.006
以甲基氢二氯硅烷、甲基乙烯基二氯硅烷为原料,采用氨解反应以及热聚合反应合成了一系列乙烯基氢基甲基聚硅氮烷(PSZ135-170),其数均分子量(Mn)在2．9×103~1．9×105之间,单位浓度聚合物的粘度(ηred)在0．06~0．49mL/g之间.通过FTIR和1HNMR对聚硅氮烷结构进行了表...
关键词:
甲基氢二氯硅烷
,
甲基乙烯基二氯硅烷
,
聚硅氮烷
,
陶瓷前驱体
,
溶解性
,
耐热性
,
粘度
韩涛
,
张艺
,
曹巧英
,
肖文明
,
刘四委
,
池振国
,
许家瑞
高分子材料科学与工程
旋光性聚合物可以使通过它的偏振光发生偏转,在手性识别和对映体拆分、手性催化剂、液晶、生物医药、光学开关和非线性光学等领域展现出良好的应用前景。本文综述了几种利用旋光性单体缩聚合成具有光学活性高分子材料的方法,对所得聚合物的热稳定性、可溶性、旋光性等主要性能进行分析比较,得到一系列重要的结论,并对其影...
关键词:
缩聚
,
聚酯酰亚胺
,
可溶性
,
耐热性
,
光学活性