A METHOD FOR CORRECTING INTENSITY IN CONTINU-OUS SCANNING X-RAY STRESS MEASUREMENT

LI Jiabao , HANG Zengqiao National Laboratory for Fatigue and Fracture of Materials , Institute of Metal Research , Academia Simca.Shenyang , China HE Jiawen Xi'an Jiaotong University , Xi'an , China

金属学报(英文版)

A set of absorption curves was priorly prepared on transparent films to fit the background and peak intensities in continuous scanning X-ray stress measurement.It may be better to correct both background and absorption of pure diffraction intensity.Experimental results revealed this to be a reliable correction method.

关键词: X-ray diffraction , null , null , null

铍材中子衍射应力测试的参数及其优化

董平 , 王虹 , 李建 , 孙光爱 , 廖哲 , 杨江荣

稀有金属材料与工程

利用铍环焊接样品进行了铍材在稳态堆上中子衍射应力测试的参数及其优化研究.结果表明:在中子束波长0.1587 nm和中子注量率2×106 n·cm-2·s-1的条件下,铍材中子衍射应力测试可以选取Be(110)晶面,衍射角为88.2°,规范体积为2 mm ×2 mm ×2 mm,初次测试采用时间为120 s,对单点进行4次重复性测试,表明衍射强度计数存在明显波动,测试应变的最大偏差接近300 με,延长时间至6000 s后测试,表明衍射曲线较为平滑,重复性好,测试应变的最大偏差减小至50με以内,相应铍材的应力测试精度约15 MPa;利用优化参数对焊接铍环焊缝附近的环向应变进行了测试,表明分布规律与国外文献报道趋势基本一致,进一步开展铍材的中子衍射应力测试奠定了基础.

关键词: 铍 , 中子衍射 , 应力测试