采用HDDR及氮化工艺制备了Sm2Fe16.5Ti0.5Ny粉末.铸态Sm2Fe16.5Ti0.5合金存在择优取向,Sm2(Fe,Ti)17主相的214衍射峰增强.均匀化退火后,只有约0.6%的α-Fe(Ti)相与主相Sm2(Fe,Ti)17共存.经不同循环的HDDR工艺处理后,物相组成不发生变化,但α-Fe(Ti)相含量增加.HDDR工艺有助于获得细晶结构,提高磁粉的矫顽力.HDDR处理的合金的氮化由初期的Sm-Fe-Ti合金与氮快速反应阶段及后期氮在合金中的均匀化扩散阶段组成.随着氮化时间的延长,富铁相含量增加.氮化物中Sm2(Fe,Ti)17Ny主相的晶格膨胀行为由HDDR与氮化工艺共同决定.在500℃氮化2h后,796kA/m最大外场下得到的最大矫顽力为164.9kA/m,氮化12h时后得到最大剩磁45.7Am2/kg.
关键词:
Sm2Fe16.5Ti0.5
,
HDDR
,
结构
,
氮化
,
磁性能
K.Yagi
金属学报(英文版)
A Materials Risk Information Platform is being developed under the cooperation of companies and academic societies with NIMS as project core. To combine safety and economy, which are sometimes contrary to each other, it is important to find an optimal solution using a new concept: risk based engineering. A 5-year project, the Materials Risk Information Platform, was started in 2001 in NIMS on the boilers of thermal power plants and the objectives of this project, research areas and its present state were outlined.