YANG Ying
,
YAN Qing-zhi
,
MA Rong
,
GE Chang-chun
钢铁研究学报(英文版)
Ferritic/martensitic (F/M) steels have been recommended as one of the candidate materials for supercritical water cooled reactor (SCWR) in-core components use for its high thermal conductivity, low thermal expansion coefficient and inherently good dimensional stability under irradiation condition in comparison to austenitic steel. CNS-Ⅱ F/M steel which has good mechanical properties was one of the 9-12Cr F/M steels designed for SCWR in the previous work. In this study a modified CNS-Ⅱ F/M steel was used and it′s ultimate tensile strength was 925 MPa at room temperature and 483 MPa at 600 ℃ after optimizing heat treatment parameter. The ductile to brittle transition temperature of modified CNS-Ⅱ F/M steel is -55 ℃. Those are at the same level or even higher than that of CNS-Ⅱ and some commercial F/M steels nominated for SCWR in-core component use. The transmission electron microscope (TEM) results showed that the mechanical properties of the tempered martensite was closely related to the decomposition stage of the martensite.
关键词:
supercritical water reactor
,
ferritic/martensitic steel
,
cladding material